2. Thermal PET Lamination Films

2.1 Gloss & Matt Type

Product Features

  • PKC’s Thermal PET Lamination Films are supplied as Roll film and Pouch film for various kinds of final application, and we can supply any chemical composition of thickness among 12~350 Microns and any sizes over 200 kinds as per demand from the customers in every market requirement of the world.

[ 32MIC GLOSS ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 32 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 500 ASTM
D-882
TD 570
ELONGATION
AT BREAK		 MD % 120 ASTM
D-882
TD 80
WORKING TEMP.   F
C		 212~248  
100~120

[ 32MIC MATT ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 32 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 460 ASTM
D-882
TD 540
ELONGATION
AT BREAK		 MD % 110 ASTM
D-882
TD 76
WORKING TEMP.   F
C		 212~248  
100~120

[ 38MIC GLOSS ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 38 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 560 ASTM
D-882
TD 600
ELONGATION
AT BREAK		 MD % 134 ASTM
D-882
TD 92
WORKING TEMP.   F
C		 212~248  
100~120

[ 38MIC MATT ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 38 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 510 ASTM
D-882
TD 560
ELONGATION
AT BREAK		 MD % 126 ASTM
D-882
TD 80
WORKING TEMP.   F
C		 212~248  
100~120

[ 42MIC GLOSS ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 42 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 630 ASTM
D-882
TD 740
ELONGATION
AT BREAK		 MD % 140 ASTM
D-882
TD 95
WORKING TEMP.   F
C		 212~248  
100~120

[ 42MIC MATT ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 42 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 580 ASTM
D-882
TD 700
ELONGATION
AT BREAK		 MD % 130 ASTM
D-882
TD 88
WORKING TEMP.   F
C		 212~248  
100~120

[ 75MIC GLOSS ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 75 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 820 ASTM
D-882
TD 950
ELONGATION
AT BREAK		 MD % 153 ASTM
D-882
TD 110
WORKING TEMP.   F
C		 212~248  
100~120

[ 75MIC MATT ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 75 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 770 ASTM
D-882
TD 880
ELONGATION
AT BREAK		 MD % 150 ASTM
D-882
TD 101
WORKING TEMP.   F
C		 212~248  
100~120

[ 125MIC GLOSS ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 125 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 970 ASTM
D-882
TD 1040
ELONGATION
AT BREAK		 MD % 160 ASTM
D-882
TD 130
WORKING TEMP.   F
C		 212~248  
100~120

[ 125MIC MATT ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 125 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 940 ASTM
D-882
TD 1020
ELONGATION
AT BREAK		 MD % 154 ASTM
D-882
TD 123
WORKING TEMP.   F
C		 212~248  
100~120

[ 250MIC GLOSS ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 250 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 1100 ASTM
D-882
TD 1170
ELONGATION
AT BREAK		 MD % 170 ASTM
D-882
TD 135
WORKING TEMP.   F
C		 212~248
100~120		  

[ 250MIC MATT ]

PROPERTIES UNIT TYPICAL VALUES TEST METHOD
AVERAGE
THICKNESS		 X-BAR ㎛ 250 mic PKC-METHOD
R-BAR 5% +/-
TREATMENT   DYNE/CM I.S 42 ↑, O.S 40 ↑  
TENSILE
STRENGTH		 MD KG/CM2 1050 ASTM
D-882
TD 1130
ELONGATION
AT BREAK		 MD % 163 ASTM
D-882
TD 131
WORKING TEMP.   F
C		 212~248
100~120		  

  • - Thermal BOPP Lamination Film – Gloss type (Model No. EM 31-1)
  • - General Application : Book cover& Prints, Photo and Papers
  • - Melting Temperature : 70 – 120℃ or less on the Laminator
     (Depend on the machine and its laminating speed)